Isocyanates and Premolymers
Milano Colori distributes SAPICI polyurethane products in the territory.
SAPICI develops and produces innovative high performance polyurethane products. In addition to its own lines of traditional products, SAPICI offers water based technology and solutions, from renewable raw materials to products with high solid content and without solvent.
ISOCYANATES
LOW FREE MONOMER
| % NV | TYPE | SOLVENT | TYPE OF ISOCYANATE | % FREE MONOMER | % NCO | Vx mPa*s @ 23° c | COLOUR GARDNER MAX | |
|---|---|---|---|---|---|---|---|---|
| POLURGREEN AD – 01 | 75 | Adduct | Ethyl acetate | TDI | < 0.1 | 12.5-13.5 | 1200-3000 | 1 |
| Characteristics: Polyurethane adduct for general uses. High compatibility with Nitrocellulose, CAB, saturated PE, vinyl and hydroxyl acrylics, bicomponent paints and enamels. The TDI content < 0.1% reduces its hazard classification. | ||||||||
| POLURGREEN AD AB – 01 | 67 | Adduct | Butyl acetate | TDI | < 0.1 | 11.5-12.1 | 400-800 | 1 |
| Characteristics: Polyurethane adduct for general uses. High compatibility with Nitrocellulose, CAB, saturated PE, vinyl and hydroxyl acrylics, bicomponent paints and enamels. The TDI content < 0.1% reduces its hazard classification. | ||||||||
| POLURGREEN HR – 01 | 50 | Isocyanurate | Butyl acetate | TDI | < 0.1 | 7.7-8.1 | 700-1400 | 1 |
| Characteristics: Fast drying and limited yellowing. Matt finish polyurethane undercoats and topcoats. This product also has applications in the hot stamping sector. The TDI content < 0.1% reduces its hazard classification. | ||||||||
| POLURGREEN OK – 01 | 60 | Mixed isocyanurate | Butyl acetate | TDI HDI | < 0.1 | 9.8-10.3 | 500-1100 | 1 |
| Characteristics: Excellent hardness, good elasticity, high resistance to yellowing, good compatibility with Nitrocellulose, brushable paints and enamels for wood, enamels with good colour retention for metals and plastic. | ||||||||
| POLURGREEN FP75 – 01 | 75 | Adduct | Ethyl acetate | TDI | < 0.1 | 12.5-13.5 | 1200-3000 | 1 |
| Characteristics: Polyurethane adduct for bicomponent adhesives and inks. The product complies with EU, BFR and FDA regulations for food packaging. The TDI content < 0.1% reduces its hazard classification. | ||||||||
HIGH SOLID
| % NV | TYPE | SOLVENT | TYPE OF ISOCYANATE | % FREE MONOMER | % NCO | Vx mPa*s @ 23° c | COLOUR GARDNER MAX | ||
|---|---|---|---|---|---|---|---|---|---|
| POLURGREEN ES | 65 | Isocyanurate | Ethyl acetate | TDI | < 0.5 | 11.1-11.5 | 250-450 | 1 | |
| Characteristics: Fast drying. Low viscosity. High solid polyurethane undercoats and topcoats. The high NCO % allows the correct cross-linking of resins with a high number of OH | |||||||||
| POLURGREEN XP AB | 70 | Isocyanurate | Butyl acetate | TDI | < 0.5 | 12.5-13.5 | 800 -2000 | 1 | |
| Characteristics: Fast drying. Low viscosity. High flexibility. Isocyanurate highly compatible with hydroxyl acrylics. Suitable for the formulation of high solid PU paints. The high NCO % allows the correct cross-linking of resins with a high number of OH. | |||||||||
| POLURGREEN ES.M | 70 | Mixed isocyanurate | Ethyl acetate | TDI HDI | < 0.5 | 12.2-12.8 | 400-800 | 1 | |
| Characteristics: Fast drying. Good Pot life. High resistance to yellowing. Excellent hardness. High solid polyurethane topcoats. The high NCO % allows the correct cross-linking of resins with a high number of OH. | |||||||||
| POLURGREEN ES.P | 75 | Mixed isocyanurate | Etil Acetate | TDI HDI | < 0.5 | 13.5-14.5 | 400-800 | 1 | |
| Characteristics: Good Pot life. High resistance to yellowing. Excellent hardness. Transparent and pigmented polyurethane gloss topcoats with high solid content. The high NCO % allows the correct cross-linking of resins with a high number of OH. | |||||||||
| POLURGREEN M 570 | 70 |
|
Butyl acetate | TDI | < 0.5 | 6.5-7.5 | 400-800 | 1 | |
| Characteristics: Fast drying, excellent hardness, elasticity and resistance to abrasion. It is used in single component paints for glossy and matt parquet. Recommended for formulation with high solid content and low viscosity. | |||||||||
AROMATIC PREPOLYMERS
| % NV | TYPE | SOLVENT | TYPE OF ISOCYANATE | % FREE MONOMER | % NCO | Vx mPa*s @ 23° c | COLOUR GARDNER MAX | ||
|---|---|---|---|---|---|---|---|---|---|
| POLURENE AD | 75 | Adduct | Ethyl Acetate |
TDI | < 0.5 | 12.5-13.5 | 1200-3000 | 1 | |
| Characteristics: Polyurethane adduct with low unreacted TDI content, for general use. High compatibility with Nitrocellulose, CAB, saturated PE, vinyl and hydroxyl acrylics, bicomponent paints and enamels. | |||||||||
| POLURENE FP75 | 75 | Adduct | Ethyl Acetate |
TDI | < 0.5 | 12.5-13.5 | 1200-3000 | 1 | |
| Characteristics: Polyurethane adduct with low unreacted TDI content, used in bicomponent systems for adhesives and inks. Complies with EU and USA regulations for products used in food packaging | |||||||||
| POLURENE AD 67 | 67 | Adduct | Xylene MPA* |
TDI | < 0.5 | 10.8-11.8 | 1200-3000 | 2 | |
| Characteristics: Polyurethane adduct with low unreacted TDI content, for general use. High compatibility with Nitrocellulose, CAB, saturated PE, vinyl and hydroxyl acrylics, bicomponent paints and enamels. | |||||||||
| POLURENE AD 67 AB LV | 67 | Adduct | Butil Acetate |
TDI | < 0.5 | 11.5-12.3 | 400-800 | 1 | |
| Characteristics: Polyurethane adduct with low unreacted TDI content, low viscosity. High compatibility with Nitrocellulose, CAB, saturated PE, vinyl and hydroxyl acrylics, bicomponent paints and enamels. | |||||||||
| POLURENE AD 72 | 70 | Adduct | Ethyl Acetate |
TDI | < 0.5 | 9.5-10.5 | 2000-3000 | 1 | |
| Characteristics: Polyurethane adduct with low unreacted TDI content, low viscosity. High compatibility with Nitrocellulose, CAB, saturated PE, vinyl and hydroxyl acrylics. More reactive and rigid than the traditional adduct. Bicomponent paints and enamels | |||||||||
| POLURENE MD 60 AB | 60 | Prepolymer | Butil Acetate |
MDI | . | 5.0-6.0 | 200-650 | 1 | |
| Characteristics: Multipurpose MDI polyisocyanate. Excellent elasticity. Good reactivity. In combination with isocyanides it improves resistance to scratching, overapplication and gives greater brilliance and softness. Improves adhesion to difficult surfaces | |||||||||
| POLURENE MD 70 AE | 70 | Prepolymer | Ethyl Acetate |
MDI | . | 9.5-9.9 | 1200-2000 | 1 | |
| Characteristics: Multi-purpose MDI Polyisocyanate. Excellent elasticity. Good reactivity. In combination with isocyanides it improves resistance to scratching, overapplication and gives greater brilliance and softness. Single component insulating paints for wood with high vegetable fat content | |||||||||
| POLURENE MD 1500 | 100 | PolISOCYANATE | – | MDI | . | 31.7-33.3 | < 100 | 18 | |
| Characteristics: Multi-purpose MDI Polyisocyanate. Excellent elasticity. Good reactivity. Particularly suitable for bicomponent polyurethane products without solvent, such as self-levelling and sealing products or in the preparation of synthetic mortars | |||||||||
| POLURENE MD 1600 | 100 | PolISOCYANATE | – | MDI | . | 31.0-32.0 | < 100 | 18 | |
| Characteristics: Multi-purpose MDI Polyisocyanate. Excellent elasticity. Good reactivity. Particularly suitable for bicomponent polyurethane products without solvent such as self-levelling, sealing and adhesive products and bicomponent primers | |||||||||
| POLURENE TPI 27 AE | 27 | PolISOCYANATE | – | TPTI | . | 7.0-7.4 | < 50 | 18 | |
| Characteristics: Polyisocyanate developed specially for the formulation of primers for melamine papers. | |||||||||
| POLURENE IR 51 AB | 50 | Isocyanurate | Butil Acetate |
TDI | < 0.5 | 7.8-8.2 | 700-1200 | 1 | |
| Characteristics: Fast drying. Limited yellowing. Matt finish polyurethane undercoats and topcoats. Low unreacted TDI content. | |||||||||
| POLURENE IR 51 AE | 50 | Isocyanurate | Butil Acetate |
TDI | < 0.3 | 7.8-8.2 | 100-400 | 1 | |
| Characteristics: Fast drying. Limited yellowing. Matt finish polyurethane undercoats and topcoats. This product also has application in the inks and adhesives sector. Low unreacted TDI content. | |||||||||
| POLURENE HRB | 50 | Isocyanurate | Butil Acetate |
TDI | < 0.5 | 7.8-8.2 | 700-1200 | 1 | |
| Characteristics: Fast drying. Limited yellowing. Matt finish polyurethane undercoats and topcoats. Low unreacted TDI content. | |||||||||
| POLURENE HRBS | 50 | Isocyanurate | Butil Acetate |
TDI | < 0.5 | 7.0-7.4 | 400-800 | 1 | |
| Characteristics: Fast drying. Limited yellowing. Good elasticity. Matt finish polyurethane undercoats and topcoats. Good compatibility with nitrocellulose. Low unreacted TDI content. | |||||||||
| POLURENE SB 50 AB | 50 | Isocyanurate | Butil Acetate |
TDI | < 0.5 | 8.0-8.4 | 200-600 | 1 | |
| Characteristics: Good flexibility. Long pot-life. Good solubility in aromatic solvents. Matt and semi-gloss finish polyurethane undercoats and topcoats. Low unreacted TDI content | |||||||||
| POLURENE KC | 50 | Mixed isocyanurate | Butil Acetate |
TDI MDI | < 0.5 – <5.0 | 7.8-8.0 | 200-400 | 1 | |
| Characteristics: Excellent elasticity and fast drying. Excellent mechanical and manual sanding properties. Improves adhesion between coats of paint. High hardness. Matt finish polyurethane undercoats and topcoats. | |||||||||
| POLURENE 3031 | 50 | Isocyanurate | Butil Acetate |
TDI | < 0.5 | 8.5-9.0 | 250-650 | 1 | |
| Characteristics: Good flexibility. Fast drying. Limited yellowing. Fair pot-life. Matt finish polyurethane undercoats and topcoats. Low unreacted TDI content. | |||||||||
| POLURENE AC 510 | 50 | Isocyanurate | Butil Acetate |
TDI | < 0.7 | 7.0-7.4 | 50-300 | 1 | |
| Characteristics: Isocyanate highly compatible with Nitrocellulose , saturated PE, vinyl and hydroxyl acrylic resins and aromatic solvents. Good elasticity. Undercoats and topcoats for wood, metal and paper. | |||||||||
| POLURENE 60 T | 60 | Isocyanurate | Butil Acetate |
TDI | < 1.0 | 9.5-9.9 | 1200-2000 | 1 | |
| Characteristics: High solid. Good flexibility. Long pot-life. Good brilliance, good compatibility with aromatic solvents and nitrocellulose. Pigmented and transparent undercoats, matt and gloss topcoats. Low unreacted TDI content | |||||||||
| POLURENE 7581 | 50 | Isocyanurate | Butil Acetate |
TDI | < 0.5 | 7.7-8.3 | 200-500 | 1 | |
| Characteristics: Isocyanate developed for application in extreme environmental conditions. Good flexibility. Fast drying. Long pot-life. Compatible with saturated polyesters, vinyl resins and nitrocellulose. Suitable for undercoats and matt topcoats | |||||||||
MIXED AROMATIC- ALIPHATIC ISOCYANATES
| % NV | TYPE | SOLVENT | TYPE OF ISOCYANATE | % FREE MONOMER | % NCO | Vx mPa*s @ 23° c | COLOUR GARDNER MAX | ||
|---|---|---|---|---|---|---|---|---|---|
| POLURENE OK.D.S | 60 | Mixed isocyanurate | Butil Acetate |
TDI HDI | < 0.5 | 10.0-11.0 | 1100-3300 | 1 | |
| Characteristics: Excellent hardness. Good elasticity. Good resistance to yellowing. Good compatibility with Nitrocellulose, fair with hydroxyl acrylic resins. Brushable paints and enamels for wood. Enamels with good colour retention for metals, plastic and other surfaces. | |||||||||
| POLURENE OK.D | 60 | Mixed isocyanurate | Butil Acetate |
TDI HDI | < 0.5 | 10.0-10.4 | 500-1100 | 1 | |
| Characteristics: Excellent hardness. Good elasticity. Good resistance to yellowing. Good compatibility with Nitrocellulose. Brushable paints and enamels for wood. Enamels with good colour retention for metal, plastic and other surfaces. | |||||||||
| POLURENE OK.D AE | 60 | Mixed isocyanurate | Ethyl Acetate |
TDI HDI | < 0.5 | 10.0-10.4 | 100-400 | 1 | |
| Characteristics: Excellent hardness. Good elasticity. Good resistance to yellowing. Good compatibility with Nitrocellulose. Brushable paints and enamels for wood. Enamels with good colour retention for metal, plastic and other surfaces. Used mainly in bicomponent adhesives and inks. | |||||||||
| POLURENE 2391 | 70 | Mixed isocyanurate | Butil Acetate |
TDI IPDI | < 0.5 | 11.7-12.0 | 800-1400 | 2 | |
| Characteristics: Good hardness. Excellent elasticity. Good resistance to yellowing. Excellent fullness and brilliance. Used for high quality pigmented and transparent polyurethane gloss topcoats. | |||||||||
| POLURENE OK-HP | 60 | Mixed isocyanurate | Butil Acetate |
TDI HDI | < 0.5 | 9.3-10.3 | 200-500 | 1 | |
| Characteristics: Excellent hardness. Good flexibility. Good resistance to yellowing. Excellent compatibility with aromatic solvents and nitrocellulose, CAB and hydroxyl acrylic resins. Suitable for polishable topcoats and enamels for wood. Enamels with good colour retention for metal, plastic and other surfaces. | |||||||||
ALIPHATIC ISOCYANATES
| % NV | TYPE | SOLVENT | TYPE OF ISOCYANATE | % FREE MONOMER | % NCO | Vx mPa*s @ 23° c | COLOUR GARDNER MAX | ||
|---|---|---|---|---|---|---|---|---|---|
| POLURENE T 70 | 70 | PolISOCYANATE Aliphatic | Butil Acetate |
IPDI | < 0.5 | 11.8-12.2 | 800-1600 | 3 | |
| Characteristics: Used for bicomponent polyurethane paints with good resistance to yellowing and outdoor conditions. In diluted form it can be used to improve the performance of low and medium oil drying resins. | |||||||||
| POLURENE T 70 AE | 70 | PolISOCYANATE Aliphatic | Ethyl Acetate |
IPDI | < 0.5 | 11.0-13.0 | 200-600 | 3 | |
| Characteristics: Used for bicomponent polyurethane paints with good resistance to outdoor conditions. In diluted form it can be used to improve the performance of low and medium oil drying resins. It has applications in bicomponent adhesives for lamination and inks | |||||||||
| POLURENE M 75 | 75 | PolISOCYANATE Aliphatic | Xylene MPA* |
HDI | < 0.2 | 16.0-17.0 | 150-310 | 1 | |
| Characteristics: Excellent for non-yellowing systems. Good flexibility. Finds application with hydroxyl acrylic resins and saturated PE for bicomponent paints and enamels for metal, wood and plastic. | |||||||||
| POLURENE MT 75 | 75 | PolISOCYANATE Aliphatic | Xylene MPA* |
HDI | < 0.2 | 16.0-17.0 | 150-310 | 1 | |
| Characteristics: Excellent for high performance non-yellowing systems. Good flexibility. Can be used in combination with hydroxyl acrylic resins and saturated polyesters for bicomponent paints and enamels for metal, wood and plastic | |||||||||
| POLURENE MT 100 | 100 | Trimero HDI | – | HDI | < 0.2 | 21.5-22.5 | 2000-3000 | 1 | |
| Characteristics: Excellent for non-yellowing systems. Good flexibility. Used extensively for high dry residue products in the sector of bicomponent paints and enamels for metal, wood and plastic | |||||||||
| POLURENE MT 100 LLV | 100 | Trimero HDI | – | HDI | < 0.2 | 22.0-24.0 | 400-800 | 1 | |
| Characteristics: Excellent for non-yellowing systems. Good flexibility. It is used mainly for bicomponent high solid paints and enamels for metal, wood and plastic. | |||||||||
| POLURENE MT 90 | 90 | Trimero HDI | Butyl acetate SOLVENT Nafta 100 | HDI | < 0.2 | 19.1-21.5 | 400-700 | 1 | |
| Characteristics: Excellent for non-yellowing systems. Good flexibility. Extensively used for high dry residue products with low viscosity in the sector of bicomponent paints and enamels for metal, wood and plastic. | |||||||||
| POLURENE MT 90 AB | 90 | Trimero HDI | Butil Acetate |
HDI | < 0.2 | 19.1-21.5 | 300-700 | 1 | |
| Characteristics: Excellent for non-yellowing systems. Good flexibility. Extensively used for high dry residue products with low viscosity in the sector of bicomponent paints and enamels for metal, wood and plastic. | |||||||||
| POLURENE MBD 2 | 75 | ISOCYANATE bloccato | SOLVENT Nafta 100 |
HDI | < 0.20 | 2500-5000 | 1 | ||
| Characteristics: Blocked isocyanate suitable for the formulation of single component non-yellowing oven-baked enamels. It can be used in traditional oven systems to increase adhesion and make more flexible. | |||||||||
ISOCYANATES DISPERSIBLE
| % NV | TYPE | SOLVENT | TYPE OF ISOCYANATE | Vx mPa*s @ 23° c | ||||
|---|---|---|---|---|---|---|---|---|
| HYDRORENE AW 1 | 100 | Aliphatic | Assente | 16.0-18.0 | 2000-4000 | |||
| Characteristics: High dispersibility. Suitable for the formulation of bicomponent water based paints with good resistance to chemicals and abrasion. Used in combination with both PUD and acrylic emulsions | ||||||||
| HYDRORENE 10 | 100 | Aliphatic | Assente | 16.9-17.9 | 2000-3600 | |||
| Characteristics: Bicomponent matt paints based on water with good to chemicals and abrasion. It is also used in the adhesives sector. Easy to disperse in acrylic and polyurethane water systems | ||||||||
| PHYDRORENE 33 | 100 | Aliphatic | Assente | 15.8-16.6 | 5000-8000 | |||
| Characteristics: Bicomponent paints based on water with good resistance to chemicals and abrasion. Easy dispersion in acrylic and polyurethane water systems. Recommended for gloss finishes | ||||||||
RESINS
LOW FREE MONOMER CONTENT
| % NV | TYPE | SOLVENT | TYPE OF ISOCYANATE | % FREE MONOMER | % NCO | Vx mPa*s @ 23° c | COLOUR GARDNER MAX | |
|---|---|---|---|---|---|---|---|---|
| UCOPOL M 505 | 53 | Prepolymer | Ethyl acetate Butile Acetate |
TDI | < 0.5 | 4.4-5.2 | < 50 | 1 |
| Characteristics: Ready-to use hygrosetting prepolymer. Excellent flexibility. Resistant to chemicals. Paints for wood, plastic, concrete, rubber, fabric and leather. | ||||||||
| UCOPOL M 541 | 100 | Prepolymer | – | TDI | < 0.5 | 3.0-4.0 | 4000-8000 | 2 |
| Characteristics: Prepolymer used to formulate single and bicomponent industrial sealants and adhesives. Can be mixed with the more rigid version (M 551) to obtain flexibility and faster drying characteristics. | ||||||||
| UCOPOL M 551 | 100 | Prepolymer | – | TDI | < 0.5 | 4.0-5.0 | 5000-9000 | 2 |
| Characteristics: Prepolymer used to formulate single and bicomponent industrial sealants and adhesives. Can be mixed with the slightly more elastic version (M 541) to obtain flexibility and faster drying characteristics. | ||||||||
| UCOPOL M 602 | 100 | Prepolymer | – | MDI | . | 22.0-24.0 | < 200 | 18 |
| Characteristics: Primer for cement. Good spreading and wettability, solventless and odourless. | ||||||||
| UCOPOL M 603 | 100 | Prepolymer | – | MDI | . | 23.0-25.0 | < 200 | 18 |
| Characteristics: Primer for cement. Good spreading and wettability, solventless and odourless. Short cross-linking time compared to the M 602 | ||||||||
| UCOPOL M 33 60 MPAX | 60 | Prepolymer | Xylene SOLVENT nafta 100 MPA* |
TDI | < 0.5 | 5.5-6.5 | 250-500 | 1 |
| Characteristics: Fast drying. Excellent hardness. Good elasticity. Paints for parquet, dust protection for industrial flooring. Polyurethane paints resistant to abrasion. | ||||||||
| UCOPOL M 34 60 MPAX LV | 60 | Prepolymer | Xylene MPA* |
TDI | < 0.3 | 6.8-7.8 | 800-1600 | 1 |
| Characteristics: Fast drying. Excellent hardness. Good elasticity. Paints for parquet, dust protection for industrial flooring. Polyurethane paints resistant to abrasion. | ||||||||
| UCOPOL M 4054 | 60 | Prepolymer | Xylene MPA* |
TDI | < 0.5 | 6.3-6.8 | 250-750 | 2 |
| Characteristics: Hygrosetting prepolymer with excellent surface hardness, resistant to abrasion, good brilliance. Fast drying. Paints for parquet and plastic. | ||||||||
| UCOPOL M 2851 | 60 | Prepolymer | Xylene MPA* |
TDI | < 0.5 | 5.0-6.0 | 600-1200 | 1 |
| Characteristics: Good elasticity. Resistant to abrasion. Paints for parquet, non-slip floors, gymnasiums. Also finds application as an impregnating agent for the protection against damp. | ||||||||
| UCOPOL W 708 | 65 | Prepolymer | Xylene MPA* |
HDI | < 0.5 | 10.0-11.0 | 300-700 | 2 |
| Characteristics: Fast drying. Excellent flexibility. Resistant to yellowing. Resistant to atmospheric and chemical agents. Paints for wood, plastic and concrete. | ||||||||
OLEOURETHANE RESINS
| % NV | SOLVENT | TYPE ISOCYANATE | OIL | Vx mPa*s @ 23° c | N.A. max | COLOUR GARDNER MAX | |
|---|---|---|---|---|---|---|---|
| UCOPOL OL 17 60 OD | 60 | Dearomatized white spirit | Aromatic | Drying agent | 3000-7000 | 1 | 6 |
| Characteristics: Good resistance to outdoor conditions. Resistant to abrasion. Paints for fittings and boats. Impregnating products for wood. Rustproofing paints. Resin obtained from renewable materials. | |||||||
| UCOPOL OL 18 50 OD | 50 | Dearomatized white spirit | Aromatic | Drying agent | 4000-7000 | 0.3 | 6 |
| Characteristics: Good hardness. Fast drying. Fair resistance to outdoor conditions. Easy matting. Impregnating agents for wood. Rustproofing paints. Resin obtained from renewable materials. | |||||||
| UCOPOL OL 18 50 X | 50 | Xylene | Aromatic | Drying agent | 4000-7000 | 0.3 | 6 |
| Characteristics: Good hardness. Fast drying. Fair resistance to outdoor conditions. Easy matting. Impregnating agents for wood. Rustproofing paints. Resin obtained from renewable materials | |||||||
| UCOPOL OL 89 55 OD | 55 | Dearomatized white spirit | Aromatic | Acidi grassi speciali | 800-1600 | 3 | 6 |
| Characteristics: Good resistance to outdoor conditions. Resistant to abrasion. Paints for fittings and boats. Impregnating agents for wood. Rustproofing paints. Resin obtained from renewable materials | |||||||
| UCOPOL OL 51 60 OD | 60 | Dearomatized white spirit | Aromatic | Acidi grassi speciali | 4000-7000 | 4 | 6 |
| Characteristics: : Good resistance to outdoor conditions. Fast drying. High quality matt and gloss paints. Easy to paint over. Resin obtained from renewable materials. |
|||||||
| UCOPOL OL W 41 55 OD | 55 | Dearomatized white spirit | Aliphatic | Acidi grassi speciali | 4000-7000 | 4 | 6 |
| Characteristics: Excellent resistance to outdoor conditions. Excellent hardness. Good resistance to chemicals. White and light coloured enamels for the construction and nautical sectors. Non-yellowing enamels with excellent filling power. Resin obtained from renewable materials. | |||||||
| UCOPOL OL 100 | 100 | – | Aromatic | Drying agent | 10000-16000 | 4 | 6 |
| Characteristics: Excellent wetting of the pigments. Particularly suitable for the formulation of printing inks and pigmented pastes. Can be used in the formulation of high solid enamels and impregnating agents for wood. Resin obtained from renewable materials. | |||||||
ELASTOMERS
| % NV | SOLVENT | TYPE ISOCYANATE | OIL | Vx mPa*s @ 23° c | N.A. max | COLOUR GARDNER MAX | |
|---|---|---|---|---|---|---|---|
| UCOFLEX EW 810/30 A | 30 | Elastomer | Aromatic | Drying agent | 1000-2000 | 1 | 6 |
| Characteristics: Transparent and pigmented paints for ABS, PVC, PUR, polystyrene and paper. Resistant to yellowing, good resistance to abrasion and knocks. | |||||||
LOW OIL ALKYD RESINS
| % NV | SOLVENT | % OIL | OIL | Vx mPa*s @ 23° c | N.A. max | N OH | % OH | COLOUR GARDNER MAX | |
|---|---|---|---|---|---|---|---|---|---|
| REXIN HS 0685 AB | 85 | Butil Acetate |
33 | Vegetable fatty acids | 500-1500 | 10 | 150 | 4.54 | 5 |
| Characteristics: Excellent hardness. Good release of solvents. Long pot-life. Matt, transparent and pigmented polyurethane topcoats. Product suitable for the formulation of high solid products. | |||||||||
| REXIN HS XP 2109 | 80 | Butil Acetate |
34 | Vegetable fatty acids | 1000-2000 | 8 | 120 | 3.60 | 6 |
| Characteristics: Fast drying. Excellent adherence to the surface. Excellent hardness. Good solvent release. Recommended for formulations to be applied in extreme environmental conditions. Product suitable for the formulation of high solid products | |||||||||
| REXIN DS 213/75 AB | 75 | Butil Acetate |
31 | Vegetable fatty acids | 1100-3300 | 12 | 100 | 3.03 | 5 |
| Characteristics: Long pot-life. Excellent filling and sanding properties. Excellent release of solvents. Very dry undercoats and topcoats for spraying and thin applications. Used as plasticiser of Nitrocellulose. | |||||||||
| REXIN DS 213 /75X | 75 | Xylene | 31 | Vegetable fatty acids | 5000-10000 | 12 | 100 | 3.03 | 5 |
| Characteristics: Long pot-life. Excellent filling and sanding properties. Excellent release of solvents. Very dry undercoats and topcoats for spraying and thin applications. Used as plasticiser of Nitrocellulose | |||||||||
| REXIN HS 129/70 AB | 70 | Butil Acetate |
32 | Vegetable fatty acids | 3000-7000 | 18 | 90 | 2.73 | 6 |
| Characteristics: Fast drying, excellent release of solvents. In combination with more plastic resins in the formulation of polyurethane undercoats improves sanding properties, alone in matt polyurethanes to obtain hardness and good spreading. | |||||||||
| REXIN HS 129 | 60 | Xylene | 32 | Vegetable fatty acids | 10000-22000 | 16 | 60 | 1.82 | 5 |
| Characteristics: Fast drying, excellent release of solvents. In combination with more plastic resins in the formulation of polyurethane undercoats improves sanding properties, alone in matt polyurethanes to obtain hardness and good spreading | |||||||||
| REXIN DS 256/75X | 75 | Xylene | 25 | Saturated fatty acids | 4000-7000 | 13 | 130 | 3.94 | 3 |
| Characteristics: Excellent brilliance. Good hardness and elasticity. Excellent resistance to yellowing. High quality nitro enamels. Transparent and pigmented polyurethane paints. Used in combination with melamine resins for oven-dried products. | |||||||||
| REXIN 1561 | 60 | Xylene | 39 | Vegetable fatty acids | 4500-8500 | 9 | 80 | 2.42 | 5 |
| Characteristics: Fast drying, Excellent hardness and good fullness. For matt polyurethane undercoats for indoor use. Finds application as a plasticiser in Nitrocellulose. Used in combination with ureic and melamine resins for oven-dried enamels. | |||||||||
| REXIN 1561/70 AB | 70 | Butil Acetate |
39 | Vegetable fatty acids | 5000-9000 | 9 | 93 | 2.82 | 5 |
| Characteristics: Fast drying, excellent hardness and good fullness. For matt polyurethane undercoats for indoor use. Finds application as a plasticiser in Nitrocellulose. Used in combination with ureic and melamine resins for oven-dried enamels. | |||||||||
| REXIN 143 | 60 | Xylene | 43 | Castor oil | 1500-3500 | 15 | 90 | 2.72 | 6 |
| Characteristics: Good flexibility. Fast drying. Good solvent release. Good wettability of pigment loads. Pigmented undercoats and topcoats. Can be used for nitrocellulose or acid catalysis systems. | |||||||||
| REXIN 143/70 AB | 70 | Butil Acetate |
43 | Castor oil | 2500-4500 | 18 | 105 | 3.18 | 5 |
| Characteristics: Good flexibility. Fast drying. Good solvent release. Good wettability of pigment loads. Pigmented undercoats and topcoats. Can be used for nitrocellulose or acid catalysis systems | |||||||||
| REXIN 2039 | 50 | Xylene MEK |
31 | Vegetable fatty acids | 7000-13000 | 20 | 80 | 2.42 | 3 |
| Characteristics: Fast drying, Excellent surface hardness, good filling capacity. Recommended for high quality undercoats and matt or gloss topcoats. Used in combination with ureic and melamine resins for oven-dried products | |||||||||
| REXIN 160 | 60 | Xylene | 57 | Castor oil | 1500-2500 | 9 | 85 | 2.57 | 5 |
| Characteristics: Good solvent release. Fast drying. Excellent wettability of pigment loads. Transparent and pigmented polyurethane paints. High pigment load undercoats | |||||||||
| REXIN 1543 | 60 | Xylene | 52 | Castor oil | 1500-3000 | 9 | 105 | 3.18 | 5 |
| Characteristics: Good solvent release. Fast drying. Excellent wettability of pigment loads. Transparent and pigmented polyurethane paints. High pigment load undercoats | |||||||||
| REXIN LS 124 | 70 | Xylene | 60 | Castor oil | 800-1600 | 10 | 120 | 3.03 | 5 |
| Characteristics: High elasticity. Low viscosity. Excellent adhesion. Excellent wettability of pigments. Pigmented polyurethane undercoats and topcoats. Paints resistant to abrasion. | |||||||||
| REXIN AP 572 | 80 | Xylene | 27 | Saturated fatty acids | 4000-9000 | 12 | 110 | 3.33 | 3 |
| Characteristics: Excellent brilliance. Excellent hardness. High resistance to yellowing. Transparent and pigmented polyurethane paints. Oven-dried enamels with high elasticity and hardness. Very dry paints. | |||||||||
| REXIN 2268 | 80 | Xylene | 27 | Saturated fatty acids | 3000-6000 | 15 | 110 | 3.33 | 1 |
| Characteristics: Resistance to yellowing similar to the best hydroxyl acrylic resins. Excellent brilliance, filling, spreading and wetting of the pigments. Highly compatible with hydroxyl acrylic resins. To formulate transparent and pigmented gloss non-yellowing paints for wood and bodywork. Ideal for white pigmented pastes. | |||||||||
| REXIN HG 70 | 70 | Xylene | 27 | Saturated fatty acids | 1300-3000 | 15 | 90 | 2.73 | 4 |
| Characteristics: Excellent brilliance, fullness and colour retention. Fast solvent release. Fast drying. Brilliant paints for indoors and outdoors. | |||||||||
| REXIN 590 | 60 | Xylene | 28 | Vegetable fatty acids | 2000-3500 | 10 | 85 | 2.57 | 4 |
| Characteristics: Good hardness and elasticity. Excellent colour retention. Good fast drying. Fast solvent release. Resistant to overspraying. Transparent and pigmented PU paints for indoors and outdoors. | |||||||||
| REXIN 590/70 AB | 70 | Butil Acetate |
28 | Vegetable fatty acids | 2600-3600 | 12 | 100 | 3.03 | 2 |
| Characteristics: Good hardness and elasticity. Excellent colour retention. Good fast drying. Fast solvent release. Resistant to overspraying. Transparent and pigmented PU paints for indoors and outdoors. | |||||||||
| REXIN CM65 | 65 | Xylene | 29 | Vegetable fatty acids | 4000-7000 | 14 | 95 | 2.88 | 3 |
| Characteristics: Good hardness and elasticity. Excellent colour retention. Good fast drying. Fast solvent release. Resistant to overspraying. Transparent and pigmented PU paints for indoors and outdoors. | |||||||||
| REXIN 2281/70X | 70 | Xylene | 40 | Vegetable fatty acids | 800-1400 | 12 | 85 | 2.57 | 5 |
| Characteristics: Resin for universal pigmented pastes. Compatible with low-medium-high oil alkyd resins, saturated polyesters, acrylics, compatible with unsaturated polyester resins and resins soluble in water.. | |||||||||
| REXIN 256 AB | 75 | Butil Acetate |
25 | Saturated fatty acids | 1000-3000 | 10 | 140 | 4.24 | 3 |
| Characteristics: Binding agent for universal pigmented pastes. Excellent brilliance. High hardness and elasticity. Excellent resistance to yellowing. Suitable for transparent and pigmented paints. Can be used in combination with ureic and melamine resins for oven-baked enamels. | |||||||||
| REXIN HG 3 | 80 | Xylene | 32 | Saturated fatty acids | 35000-45000 | 20 | 125 | 3.79 | 1 |
| Characteristics: Brilliant transparent and white topcoats with excellent body. Fast drying and good resistance to yellowing. | |||||||||
| REXIN HG 7 | 80 | Xylene | 34 | Saturated fatty acids | 40000-50000
@25°C |
12 | 120 | 3.64 | 1 |
| Characteristics: Resin for high quality gloss topcoats with excellent body, levelling and resistance to yellowing | |||||||||
| REXIN 138 | 80 | Butil Acetate |
37 | Vegetable fatty acids | 30000-50000 @25°C |
14 | 132 | 3.96 | 3 |
| Characteristics: Suitable for matt 2k PU topcoats with a perfect balance between hardness and flexibility. Its high level of cross-linking guarantees fast drying. | |||||||||
| REXIN 5380 | 70 | Xylene | 33 | Vegetable fatty acids | 25000-35000 @25°C |
14 | 115 | 3.48 | 3 |
| Characteristics: Resin recommended for high quality undercoats thanks to the excellent wetting of the surfaces that guarantees a perfect filling of the pore and excellent levelling. Long pot-life | |||||||||
SATURATED POLYESTERS
| % NV | SOLVENT | Vx mPa*s @ 23° c | N.A. max | N OH | % OH | COLOUR GARDNER MAX | ||
|---|---|---|---|---|---|---|---|---|
| REXIN HSP 05100 | 100 | – | 24000-32000 | 15 | 210 | 2.27 | 3 | |
| Characteristics: Excellent hardness. High resistance to chemicals. Excellent resistance to abrasion. Excellent spreading. Transparent and pigmented 2k PU paints with high brilliance. Product suitable for the formulation of high solid products. | ||||||||
| REXIN DP 127 | 70 | Butil Acetate |
1800-3500 | 13 | 135 | 4.09 | 2 | |
| Characteristics: Excellent hardness. Good resistance to abrasion. Excellent resistance to yellowing. Excellent wetting of pigment loads. Transparent and pigmented 2k PU paints with high brilliance and fast drying. Product recommended for the formulation of pigmented pastes | ||||||||
| REXIN DP 328 | 70 | Butil Acetate |
3000-5000 | 13 | 110 | 3.33 | 3 | |
| Characteristics: Good hardness and flexibility. Good resistance to abrasion. Good filling and good solvent release. Good compatibility with Nitrocellulose. Can be used in combination with ureic and melamine resins. Transparent and pigmented 2K PU paints. | ||||||||
| REXIN DP 343 | 60 | Xylene | 1500-3500 | 15 | 90 | 2.73 | 6 | |
| Characteristics: Good flexibility. Fast drying. Good solvent release. Good wetting of pigment loads. Pigmented undercoats and topcoats. Can be used for nitrocellulose or acid catalysis systems. | ||||||||
| REXIN DP 390 | 60 | Xylene | 2000-3500 | 10 | 85 | 2.57 | 4 | |
| Characteristics: Good flexibility and hardness. Fast drying. Long pot-life. Good resistance to overpainting. Matt and gloss transparent and pigmented 2K PU paints. | ||||||||
| REXIN DP 408/80 AB | 80 | Butil Acetate |
1000-1800 | 4 | 240 | 7.27 | 3 | |
| Characteristics: Highly branched polyester. High resistance to chemicals. Excellent hardness and resistance to abrasion. 2K PU paints for parquet. Enamels for metal | ||||||||
| REXIN DP 411 | 100 | – | 20000-40000 | 4 | 180 | 5.61 | 2 | |
| Characteristics: Slightly branched polyester without solvents. Good resistance to chemicals. Good hardness. Excellent elasticity. 2K PU paints for parquet. | ||||||||
| REXIN DP 412 | 100 | – | 3500-6500 | 4 | 185 | 5.61 | 2 | |
| Characteristics: Slightly branched polyester without solvents. High resistance to chemicals. Excellent elasticity. Paints and enamels for metal, wood and plastic and rubber materials | ||||||||
| REXIN DP 417 | 100 | – | 10000-20000 | 5 | 40 | 1.20 | 2 | |
| Characteristics: Polyester resin without solvents. Excellent elasticity. Suitable for paints and enamels for paper, leather, plastic and rubber. Used in the formulation of soft-touch effect paints. | ||||||||
| REXIN DP 430 | 100 | – | 7000-11000 @25°C |
4 | 55 | 1.67 | 1 | |
| Characteristics: Polyester resin without solvents. Excellent elasticity. Suitable for paints and enamels for paper, leather, plastic and rubber. Used in the formulation of soft-touch effect paints | ||||||||
| REXIN DP 202 | 80 | nButanolo Isopropanolo |
< 2000 | 85-115 | 400 | 12.12 | 2 | |
| Characteristics: Polyether without silicone used as an additive (2-3%) in oven process systems and primers for significantly improved adhesion. Also helps to improve resistance to atmospheric agents. | ||||||||
WATER-BASED POLYURETHANE DISPERSIONS
| % NV | TYPE OF ISOCYANATE | SOLVENT | Vx mPa*s @ 23° c | PH | |
|---|---|---|---|---|---|
| BLUEPUR 2937 | 36 | Aliphatic | Coalescent free | 250 max | 7.5-8.5 |
| Characteristics: Resin for 1K and 2K water-based systems. This resin has a self-cross-linking which produces a high level of hardness. Fast drying. Can be used to formulate transparent and pigmented paints | |||||
| BLUEPUR 3037 | 36 | Aliphatic | Coalescent free | 250 max | 7.5-8.6 |
| Characteristics: Resin for 1K and 2K water-based systems. This resin has a self-cross-linking which produces a high level of hardness. The high flexibility makes the resin suitable for the formulation of paints for plastic and metal | |||||
| BLUEPUR 3080 | 36 | Aliphatic | Coalescent free | 250 max | 7.5-8.7 |
| Characteristics: Resin for 1K and 2K water-based systems. Its special structure allows this resin to be used to improve the coalescence of PUD and acrylic emulsions. The high elasticity makes the resin suitable for the formulation of paints for leather and fabrics. | |||||
POLYESTERS FROM RENEWABLE SOURCES
| STRUCTURE | Mw | N OH | N.A. MAX | Vx mPa*s | |
|---|---|---|---|---|---|
| REXIN XP 84 D | Linear | 500 | 212 | < 1 | 1700 @ 25°C |
| Characteristics: Linear polyol polyester with high endurance and resistance to chemicals. Excellent flexibility and resistance to atmospheric agents. Developed to give the same performance as synthetic petroleum products in the final application and use. | |||||
| REXIN XP 84 M | Linear | 1000 | 112 | < 1 | 730 @ 60°C |
| Characteristics: Linear polyol polyester with high endurance and resistance to chemicals. Excellent flexibility and resistance to atmospheric agents. Developed to give the same performance as synthetic petroleum products in the final application and use. | |||||
| REXIN XP 84 MM | Linear | 2000 | 56 | < 1 | 3700 @ 60°C |
| Characteristics: Linear polyol polyester with high endurance and resistance to chemicals. Excellent flexibility and resistance to atmospheric agents. Developed to give the same performance as synthetic petroleum products in the final application and use. | |||||
| REXIN XP 821 B | Branched | 2200 | 61 | 1.4 | 3150 @ 60°C |
| Characteristics: Polyol polyester with succinic acid branches for applications in the foam sector. Makes it possible to obtain products with high content of material from renewable sources. | |||||
| REXIN XP 821 HB | Branched | 2300 | 64 | 1.2 | 4000 @ 60°C |
| Characteristics: Polyol polyester with succinic acid branches for applications in the foam sector. Makes it possible to obtain products with high content of material from renewable sources | |||||
| REXIN XP 81 | Linear | 1000 | 107 | 0.5 | 3700 @ 25°C |
| Characteristics: Polyol polyester with succinic acid branches for applications in the foam sector. Makes it possible to obtain products with high content of material from renewable sources. | |||||
| REXIN XP 82 | Linear | 1000 | 113 | 0.8 | 9000 @ 25°C |
| Characteristics: Polyol polyester with succinic acid branches for applications in the elastomers, paints and adhesives sector. Makes it possible to obtain products with high content of material from renewable sources. | |||||
| REXIN XP 86 | Linear | 1000 | 108 | 0.7 | 6000 @25°C |
| Characteristics: Polyol polyester with succinic acid branches for applications in the elastomers, paints and adhesives sector. Makes it possible to obtain products with high content of material from renewable sources. | |||||
PREPOLYMERS
| TYPE | Vx mPa*s @ 23° c | % MONOMER | % NCO | |
|---|---|---|---|---|
| POLURENE 450 | Polyether – TDI | 5000-9000 @ 23° C |
< 0.5 | 4.5 |
| Characteristics: Linear prepolymer with high elongation and resistance to traction | ||||
| POLURENE 620 | Polyether – TDI | 15000-25000 @ 23° C |
< 0.5 | 6.2 |
| Characteristics: Linear prepolymer with high elongation and resistance to traction. | ||||
| POLURENE 750 | Polyether – TDI | 8000-12000 @ 40° C |
< 0.5 | 7.5 |
| Characteristics: Linear prepolymer with high elongation and resistance to traction | ||||
| POLURENE PE 95 A | Polyether – TDI | 250-450 @ 70° C |
< 0.1 | 6.0 |
| Characteristics: Prepolymer based on PTMEG with high resistance to oxidation and UV. | ||||
| POLURENE PE 70 D | Polyether – TDI | 350-550 @ 70° C |
< 0.1 | 8.4 |
| Characteristics: Prepolymer based on PTMEG with high resistance to oxidation and UV. | ||||
| POLURENE PET 95 A | Polyester – TDI | 1500-1700 @ 70° C |
< 0.1 | 5.4 |
| Characteristics: Prepolymer with high resistance to solvents and to traction. | ||||
| POLURENE PET 85 A | Polyester – TDI | 2400-3000 @ 70° C |
< 0.1 | 3.6 |
| Characteristics: Prepolymer with high resistance to solvents and to traction. | ||||
| POLURENE XP 4217 | Polietere – MDI | 8000-10000 @ 40° C |
< 1 | 4.5 |
| Characteristics: Prepolymer based on MDI with low free monomer content | ||||
| POLURENE XP 3617 | Polyether – TDI | 4500-6500 @ 40° C |
< 1 | 10.5 |
| Characteristics: Prepolymer based on TDI developed for the preparation of products without R40. | ||||
| POLURENE XP 4041 | Polietere – HDI | 2000-4000 @ 23° C |
< 0.5 | 9.5 |
| Characteristics: Aliphatic prepolymer for applications where maximum resistance to yellowing is necessary | ||||
| POLURENE 506 | Polietere – MDI | 500-1500 @ 23° C |
. | 2.2-2.6 |
| Characteristics: Hydrophilic prepolymer in DBE used as a water sequestrant. Used to prevent extensive infiltration in civil engineering works | ||||
| POLURENE 604 | Polietere – MDI | 4000-8000 @ 23° C |
. | 9.0-10.0 |
| Characteristics: Branched prepolymer used to achieve a high density of cross-linking | ||||
| POLURENE 609 | Polietere – MDI | 600-1400 @ 23° C |
. | 14.0-14.7 |
| Characteristics: Low viscosity aromatic polyurethane prepolymer, used in the formulation of products with high final elasticity | ||||
ADHESIVES
BLOCKED ISOCYANATES
| % NV | % NCO | Vx mPa*s @ 23° c | COLOUR GARDNER MAX | |
|---|---|---|---|---|
| POLURENE LP 100 LV | 100 | 0.2 | 25000-45000 | 1 |
| Characteristics: Polyurethane prepolymer based on TDI with blocked isocyanic groups. Low viscosity compared to POLURENE LP 100. Excellent epoxy flexibilizer. Excellent flow properties | ||||
| POLURENE LP 90 LV | 90 | 0.2 | 10000-25000 | 1 |
| Characteristics: Polymer based on branched TDI, 90% in dioctyl adipate, containing blocked isocyanic groups with cross-linking potential. Very low viscosity. Epoxy flexibilizer for adhesives and sealants. Excellent flow properties and easy to use | ||||
| POLURENE LP 80 LV | 80 | 0.2 | 7000-12000 | 1 |
| Characteristics: Polymer based on branched TDI, 80% in dioctyl adipate, containing blocked isocyanic groups with cross-linking potential. Very low viscosity. Epoxy flexibilizer for adhesives and sealants. Excellent flow properties and easy to use | ||||
| POLURENE BK 50 AE | 50 | 0.1 | < 100 | 2 |
| Characteristics: Polymer based on TDI, containing blocked isocyanic groups with cross-linking potential when heated. Ideal for bonding TNT, PVC, various fabrics and finishing | ||||
| POLURENE LP 1810 | 100 | 0.2 | 25000-45000 | 1 |
| Characteristics: Polymer based on TDI, containing blocked isocyanic groups. Used in combination with aliphatic diamines for the formulation of paints without solvent and high thickness and primer for the automotive sector. | ||||
| POLURENE LP 100 NFF | 100 | 0.2 | 25000-45000 | . |
| Characteristics: Polyurethane prepolymer based on TDI with blocked isocyanic groups. Epoxy flexibilizer for adhesives and sealants. Excellent flow properties. This product does not release nonylphenol | ||||
INDUSTRIAL ADHESIVES
| % NV | % NCO | Vx mPa*s @ 23° c | COLOUR GARDNER MAX | |
|---|---|---|---|---|
| POLURENE IAX 3719 | 67 | 1.6-2.2 | 6000-10000 | 2 |
| Characteristics: Single component polyurethane adhesive based on MDI in ethyl acetate. Excellent initial set, ideal for PVC, expanded PU and natural and synthetic fabrics. | ||||
| POLURENE LPI 1272 | 100 | 12.5-13.5 | 3000-7000 | 18 |
| Characteristics: Polyurethane adhesive based on MDI without solvent. Recommended for the manufacture of sandwich panels for thermal and acoustic insulation | ||||
| POLURENE LPI 2572 | 100 | 12.5-14.5 | 3000-7000 | 18 |
| Characteristics: Polyurethane adhesive based on MDI without solvent. Recommended for the manufacture of sandwich panels for thermal and acoustic insulation | ||||
| POLURENE LPI 34 NT | 100 | 14.0-16.0 | 2000-4000 | 18 |
| Characteristics: single component adhesive for D4 approved wood, suitable for wood compensates and outdoor gluing (garden furniture). Highly resistant to acid and alkali hydrolysis. Product with a short pot- life, very crystalline and resistant to thermal shocks | ||||
| POLURENE LPI 36 | 100 | 12.5-14.5 | 3000-5000 | 3 |
| Characteristics: Single component adhesive for wood, lamellar systems and gluing outdoors (garden furniture). Highly resistant to acid and alkali hydrolysis. Short pot-life compared to Polurene LPI 34 NT. Very crystalline and resistant to thermal shocks. Recommended for assembly work where short setting times are required | ||||
| POLURENE LPI 103 | 100 | 8.0-10.0 | 200-400 (*) | . |
| Characteristics: Single component adhesive based on MDI. Excellent initial adhesion, recommended for PVC, expanded PU and natural and synthetic fabrics. (*) 75% in ethyl acetate | ||||
| POLURENE LPI 433 | 100 | 14.0 | 4000 | . |
| Characteristics: 2K adhesive system 100% dry. Excellent initial adhesion. Can be used as such or in the loaded version formulating the hydroxyl component. | ||||
| POLURENE LPI 407 | 100 | 13.0 | 13000 | . |
| Characteristics: MDI Polyester/Polyether 2K adhesive system in ethyl acetate. Excellent initial adhesion. Can be used as such or in the loaded version formulating the hydroxyl component | ||||
ADHESIVES FOR THE FOOTWEAR SECTOR
| % NV | % NCO | COLOUR GARDNER MAX | SOLVENT | ||
|---|---|---|---|---|---|
| UNI-DUR WB 7000 | 100 | 16.9 -17.1 | 2000 – 4000 | 2 | – |
| Characteristics: Catalyst for high quality water based polyurethane systems. Improves the resistance of bonding to humidity, heat and solvents. Its hydrophilic nature makes it easy to disperse by stirring | |||||
| UNI-DUR WB 7075 | 75 | 12.9 -13.1 | < 100 | 1 | Ethyl Acetate |
| Characteristics: Catalyst for high quality water based polyurethane systems. Improves the resistance of bonding to humidity, heat and solvents. Its hydrophilic nature makes it easy to disperse by stirring | |||||
| UNI-DUR E 1001 | 43 | 6.8 – 7.2 | . | 1 | Ethyl Acetate |
| Characteristics: Isocyanic hardener recommended for the cross-linking of industrial polyurethane adhesives for natural or synthetic rubber. | |||||
| UNI-DUR E 1001 RN | 40 | 7.0 – 7.6 | . | 1 | Ethyl Acetate |
| Characteristics: Improves adhesion, cohesion and resistance of the bond to heat. Minimal colour change. | |||||
| UNI-DUR E 2002 ARFE | 27 | 6.8 – 7.2 | < 50 | 18 | Ethyl Acetate |
| Characteristics: Recommended for the cross-linking of industrial polyurethane adhesives for natural or synthetic rubber. Improves adhesion, cohesion and resistance of the bonding to heat | |||||
INK SECTORS
RESINS
| % NV | SOLVENT | Vx mPa*s @ 23° c | N OH | % NCO | |
|---|---|---|---|---|---|
| UCOPOL M 33/65 K | 65 | Ethyl acetate | 400-800 | . | 5.9 |
| Characteristics: Hygrosetting polyurethane resin specially developed for application in overprint paints. The main feature is its easy use on flexography. Good wetting properties on different surfaces and inks. It is compatible with alkyd compounds, saturated polyester resins, nitrocellulose and vinyl copolymers. | |||||
| REXIN K 6302 | 70 | Ethyl acetate | 100-500 | 100 | . |
| Characteristics: Polyester resin recommended for the formulation of inks and overprint varnishes. | |||||
| REXIN K 1939 | 75 | Ethyl acetate | 3000-4000 | 165 | . |
| Characteristics: Saturated hydroxyl-terminated polyester resin particularly suitable for formulations of polyurethane overprint varnishes. When used for the formulation of inks, the cross-linked film is clear, not sticky and highly resistant to ageing, chemicals and heat. | |||||
| REXIN K 6258 | 60 | Ethyl acetate | <100 | 180 | . |
| Characteristics: Saturated branched polyester resin recommended for the formulation of inks and overprint varnishes. Compatible with nitrocellulose, urea and melamine resins. | |||||
| REXIN K 411 | 100 | 20000-30000 | 180 | . | |
| Characteristics: Saturated polyester resin with high chemical and mechanical resistance recommended for the production of high quality inks. Compatible with nitrocellulose, urea and melamine resins. | |||||
HARDENERS
| % NV | SOLVENT | Vx mPa*s @ 23° c | N OH | % NCO | |
|---|---|---|---|---|---|
| POLURENE FP 75 | 75 | Ethyl acetate | 1200-3000 | . | 13.0 |
| Characteristics: Aromatic polyurethane adduct recommended for the formulation of bicomponent inks. Used in combination with non-drying alkyd resins with low oil, hydroxyl acrylic resins, saturated polyesters and vinyl resins. Compatible with nitrocellulose and CAB. | |||||
| POLURGREEN FP 75-01 | 75 | Ethyl acetate | 1200-3000 | . | 13.0 |
| Characteristics: Aromatic polyurethane adduct with low free monomer content, recommended for the formulation of bicomponent inks. Used in combination with non-drying alkyd resins with low oil, hydroxyl acrylic resins, saturated polyesters and vinyl resins. Compatible with nitrocellulose and CAB. | |||||
| POLURENE IR 51 K | 50 | Ethyl acetate | 100-400 | . | 8.0 |
| Characteristics: Fast drying aromatic isocyanurate based on TDI with good elasticity and flexibility. Can be used in combination with saturated polyesters of the REXIN K series, for the formulation of overprint varnishes and primers. | |||||
| POLURENE OK K | 60 | Ethyl acetate | 100-400 | . | 10.2 |
| Characteristics: Mixed aliphatic aromatic isocyanurate used for the formulation of inks with good resistance to yellowing. Good elasticity and flexibility. Can be used in combination with saturated polyesters of the REXIN K series, for the formulation of overprint varnishes. | |||||